Atomic and Crystallographic |
||
|---|---|---|
|
Atomic Number |
22 |
|
|
Atomic Weight |
47.60 |
|
|
Atomic Volume |
10.64 cm3 / mol |
|
|
Lattice Type |
Body Center Cubic |
|
|
Mass |
|||
|---|---|---|---|
|
Metric |
English |
||
|
Density at 20ºC |
4.51 g/cm3 |
0.163 lb/in3 |
|
| Thermal | |||
|---|---|---|---|
|
Metric |
English |
||
|
Melting Point |
1660ºC |
3320ºF |
|
|
Boiling Point |
3285ºC |
5945ºF |
|
|
Specific Heat at 0ºC - 100ºC |
.540 J/g/ºC |
.129 BTU/lb/ºF |
|
|
Average Linear Coefficient of Expansion at 25C (68ºF - 212ºF) |
4.51 g/cm3 |
0.163 lb/in3 |
|
| Thermal Conductivity | |||
|---|---|---|---|
|
Metric |
English |
||
|
20ºC (68ºF) |
219 W/cm·K |
12.6 BTU/hr·ft·ºF |
|
| Mechanical Properties of Ti Grades 2, 7, 16 & 26 | |||
|---|---|---|---|
|
Metric |
English |
||
|
Tensile Strength (minimum) |
345 Mpa |
50,000 psi |
|
|
Yield Strength (minimum) |
276 Mpa |
40,000 psi |
|
|
Modulus of Elasticity (Tension) |
103 Gpa |
15,000,000 psi |
|
|
Nominal Hardness |
82 Hrb |
||