Atomic and Crystallographic |
||
|---|---|---|
|
Atomic Number |
40 |
|
|
Atomic Weight |
91.22 |
|
|
Atomic Volume |
10.9 cm3 / g · atom |
|
|
Lattice Type |
Body Center Cubic |
|
|
Mass |
|||
|---|---|---|---|
|
Metric |
English |
||
|
Density at 20ºC |
6.51 g/cm3 |
0.235 lb/in3 |
|
| Thermal | |||
|---|---|---|---|
|
Metric |
English |
||
|
Melting Point |
1852ºC |
3665ºF |
|
|
Boiling Point |
5425ºC |
9800ºF |
|
|
Specific Heat at 0ºC - 100ºC |
.02847 J/g/ºC |
N/A |
|
|
Average Linear Coefficient of Expansion at 25ºC (68ºF - 212ºF) |
5.8 x 10-6 mm/mm/ºC |
3.2 x 10-6 in/in/ºF |
|
| Thermal Conductivity | |||
|---|---|---|---|
|
Metric |
English |
||
|
20ºC (68ºF) |
.22 W/m·K |
13 BTU/hr·ft·ºF |
|
| Mechanical Properties of Zirconium 702 | |||
|---|---|---|---|
|
Metric |
English |
||
|
Tensile Strength (minimum) |
379 Mpa |
55,000 psi |
|
|
Yield Strength (minimum) |
207 Mpa |
30,000 psi |
|
|
Modulus of Elasticity (ASTM MIN) |
99.2 Gpa |
14,400,000 psi |
|
|
at 260ºC (500ºF) |
75.2 Gpa |
10,900,000 psi | |
TITAN Metal Fabricators | |||